Introduction to Anviloy 1150 ---Tungsten Heavy Alloy Part
Introduction to Anviloy 1150 ---Tungsten Heavy Alloy Part
Material Components : W Ni Fe Mo alloy
Anviloy 1150 ( WNiFeMo ) is a tungsten based material made using special high temperature powder metallurgy techniques. It is used in resistance welding, pressure die casting and hot extrusion dies applications. Anviloy 1150 material has a low coefficient of thermal expansion, hot erosion resistance and good thermal conductivity. Tungsten is used as a base due to its high melting point and low coefficient of thermal expansion. Elements added to the tungsten enhance machinability and ductility.
The excellent thermal conductivity of Anviloy 1150 provides an additional benefit to increase cooling in difficult to cool areas. So, Anviloy 1150 can be used to increase cooling in critical areas to minimize porosity.
Anviloy 1150 ( WNiFeMo ) was developed primarily as an alternative to H-13 Tool Steels for die cast tooling to save you time and money. With Anviloy 1150 as the base for your dies, you will get more additional benefit as:
Longer die life
Better surface finishes on products
Fewer rejects
Lower cost
Less porosity in heavy sections
Application: Hot Extrusion Dies, Die Cast Tooling, and high mass and gyro.
Machinability is similar to gray iron.
Properties of Anviloy 1150
  
|
Material Components |
Metric |
English |
|
Tungsten, W |
90.0 % |
90.0 % |
|
Iron, Fe |
2.0 % |
2.0 % |
|
Nickel, Ni |
4.0 % |
4.0 % |
|
Molybdenum, Mo |
4.0 % |
4.0 % |
|
Properties |
¡¡ |
¡¡ |
|
Density |
17.2 g/cm3 |
0.623 lb/in3 |
|
Hardness |
34 HRC |
34 HRC |
|
Ultimate Tensile Strength |
960 MPa |
140 kpsi |
|
Yield Tensile Strength |
860MPa |
120 kpsi |
|
Elongation at Break |
3 % |
3 % |
If you need any more details of the above news and/or products, please visit Chinatungsten Online, or contact us directly.
Disclaimer: The article is only reflecting the opinions of the author. We have no responsibility to prove the originality and authenticity of the content, words and/or pictures. You readers should just take it as reference and check the details by yourselves. And the content is not a suggestion for investment decision. The investor takes his or her own risks if he or she operates accordingly. If you have any dissent about the contents above, please contact the relevant author, or the webmaster. We will try our best to assist the dealing of the related issues. Thanks for your visit and cooperation.
|