| Powder |
Technical Parameter |
Specification |
Application |
| KF-2 |
HRC¡«20
Working Temperature: Max. 800¡æ
NiAl 80/20
|
Nickel clad Aluminum exothermal composite powder. High bonding strength, good oxidization resistance. Used as undercoating and service coating or restoring coating. Can form micro-metallurgical bonding with ordinary steel, alloy steel, non-corrosive steel, nitriding steel, cast-iron, cast-steel, nickel, Mg, Ti, Monel metal and NiCr alloy etc. |
Plasma Spraying
Restoring parts and used as undercoating for aviation parts, tank drive parts, combustion drive machine, crankshaft.
Bonding layer for ceramic coating. |
| KF-6 |
HRC¡«20
Working Temperature: Max. 800¡æ
Ni5Al |
Aluminum clad Nickel composite powder. Less smoke than KF-2 when spraying. Other performance is similar with KF-2. |
Plasma Spraying
Flame spraying |
| KF-110 |
HRC¡«20
Working Temperature: Max. 900¡æ
NiCr5Al |
Nickel Chromium Aluminum composite powder. As high temperature undercoating and high temperature oxidization resistance coating at 800¡æ. |
Plasma Spraying
Flame spraying
As undercoating before spraying NiCr-Cr2C3 for boiler.
Bonding layer for ceramics. |
| KF-113A |
HRC¡«20
Working Temperature: Max. 900¡æ
NiCrAl CoY2O3 |
NiCrAl CoY2O3 composite powder is used as high temperature undercoating and high temperature oxidation resistant coating at 800¡æ. |
Plasma Spraying
As bonding layer for thermal barrier coatings |
| KF-301 |
HRC¡«20-30
Working Temperature: Max. 950¡æ
Cr22Al 11Y1 Ni(Bal.) |
Nickel Chromium Aluminum Yttrium composite powder.
As high temperature bonding powder, properties are next only to CoCrAlY. |
Plasma Spraying, HVOF
As heat resistance coating of metallurgical roller, hot-dip roller, heat treated furnace roll.
As bonding layer for thermal barrier coatings of aviation fan, gas-engine blade etc. |
| KF-133 |
HRC¡«20
Working Temperature: Max. 700¡æ
NiCr5Al5Mo |
Good toughness and wear resistance properties. High bonding strength and erosion resistance. Mainly used to restore parts. The coating has good machining performance and can be grinded to high smoothness. |
Plasma Spraying
Flame spraying
Optimum for restoring parts. |
| KF-91Ni |
HRC¡«40
Working Temperature: Max. 540¡æ
W Al Cr C Ni |
A new type coating material applied for oxyacetylene flame spraying. It is a wear resistance coating with high boding strength. |
Good grain-abrasion resistance, used as roller skate parts spraying and repairing |
| KF-Ni |
HRC¡«Max. 20
Working Temperature: Max. 700¡æ
Ni¡Ý99 |
High purity Nickel powder. The coating is dense and easy to cut. Good at corrosion resistance. The placement of Monel alloy as anti-corrosion coating. |
Plasma Spraying
Flame spraying
Restoring Nickel and Nickel alloy surface parts. |
| KF-306 |
HRC¡«20
Working Temperature: Max. 900¡æ
NiCr 80/20 |
Excellent as corrosion resistance coating or as oxidation corrosion resistance coating at 900¡æ.
Bonding layer for ceramic coatings. |
Plasma Spraying
HVOF
As bonding layer for ceramic coatings or corrosion resistance coating. |
| KF-305 |
HRC¡«25
Working Temperature: Max. 900¡æ
NiCr 50/50 |
High Chromium Nickel alloy. Good at wear and corrosion resistance. Service performance is similar with NiCr 80/20. |
Plasma Spraying
HVOF
As bonding layer for ceramic coatings or corrosion resistance coating. |
| Haynes alloy |
HRC¡«20
Working Temperature: Max. 480¡æ
Ni Cr W Mo |
Excellent corrosion resistance than 316L and has certain wear resistance properties. |
Plasma Spraying
HVOF
Spraying parts under the working condition of high corrosion. |
| KF-21T |
HRC¡«60
Working Temperature: Max. 480¡æ
Ni Cg 75/25 |
Nickel clad Graphite powder. Low hardness and good lubricity. As wear resistance coating in leakage control of machine parts. Bad oxidation resistance property. |
Oxyacetylene Flame Spraying
Good for bearing lubricated coating under oil-less working condition. |
| KF-22T |
HRC¡«60
Working Temperature: Max. 480¡æ
Ni Cg 50/50 |
Nickel clad Graphite powder.
Better lubricity because of increased Graphite content.
As lubricated coating for bearing bush. |
Oxyacetylene Flame Spraying
As lubricated coating for bearing bush under oil-less working condition. |
| KF-20 |
HRC¡«60
Working Temperature: Max. 500¡æ
Ni78 MoS222 |
Nickel clad Molybdenum Disulfide powder. Wear reducing material. Good lubricating property. Working temperature is up to 500¡æ. |
Oxyacetylene Flame Spraying
Good for movable seal parts, abradable seal rings and low friction materials. |